s-2 is a product which is used to remove black oxide layer formed while s.s. welding. 

it cleans the black oxide layer formed while s.s. welding and it also helps in increasing the shine of the material post welding.

Pickling paste S-BRIGHT P-16 is used to treat stainless steel surfaces that have been damaged by working operations such as welding, forming, cutting and blasting. It removes welding oxides, the underlying chromium-depleted layer, micro-slag particles and other contaminants that may cause local corrosion.

Pickling paste S-BRIGHT P-16 is served as a chemical treatment of stainless steel and aluminum alloys after welding with the MIG/MAG and TIG methods. It is excellent at removing blooms and fire scales, which have been formed during the welding of stainless steel elements & eliminating the need of mechanical cleaning. In the case of aluminum elements, pickling serves mainly as a preparation of the surface to be painted.

 

Pickling paste is used for cleaning and passivating of welding joints and the heat affected zone (HAZ) in welded stainless steel constructions. It is based on a unique recipe in which the concentration of nitric acid is less in quantity in comparison with others.

 

Pickling paste S-BRIGHT P-16 has a real thick paste consistency which gives a very high sticking capacity making it extra suitable for cleaning in difficult positions to avoid risk of sagging.  The paste is in a gel form which is applied with a brush. The thixotropic feature of the gel gives the possibility to apply it also on vertical surfaces. Pickling paste can be used to remove black oxide, weld scale and burn marks left during the welding of stainless steel. It removes both metallic contamination and welding and heat treating scales.

 

Pickling paste is economical to use as only a thin film of the pickling paste is required for perfect result, Improved pickling result offers a brighter surface with less discolouration than classical product result. Thick viscous gel with long moisture phase the longer the moisture phase, the longer the reaction times for a better cleaner result. Pickling paste S-BRIGHT P-16 does not contain Hydrochloric or Sulphuric Acids and has a low odour (more user-friendly). Pickling paste S-BRIGHT P-16 is a very efficient (minimal to no manual cleaning afterwards only one application is needed). Pickling paste has a long shelf-life.

Process :-

 

1.   Apply Degreaser on the surface for   5- 10 minutes. Then wash the surface thoroughly with water.
2.  S-BRIGHT P-16 paste is to be applied on the weld seam and surrounding area with a brush.
3.  Leave the S-BRIGHT P-16 paste on the weld seam for 15-45 minutes depending on the thickness of the oxide scale.
4.  Scrub the surface with a plastic bristled brush and then wash surface thoroughly with water.

We offer the paste with a neutralizing paste as a set. This is recommended as the pickling paste and the paste residue are toxic and corrosive. The neutralizing of the residual pickling paste on the metal surface protects the worker from toxic substances and burning. The compounds formed during the neutralizing are inactive and neutral to humans and its surrounding. The pickling paste does not contain chloride